Abstract:
Development of nano-scale materials have been intenselly researched in the field of sensors.
The intimate correlation between nanostructured materials and sensor performance has led to
multidisciplinary state-of-art technological development in sensors technology. Metal oxide
semiconductors in particular, are of great interest in the development of gas sensors and
biomedical nanodevices. The experimental work reported in this dissertation outlines the
fabrication of nanostructured C112O and ZnO thin films using electrodeposition and their
applicability in sensing liquefied petroleum (LP) gas and glucose. The surface morphological
properties and the structural properties of the fabricated thin films were evaluated using
scanning electron microscopy and X-ray diffraction and energy dispersive X-ray spectroscopy.
The photo-response properties were assessed using photocurrent spectral response
measurements and the electrical properties were studied by Mott-Schottky measurements. LP
gas sensing was performed under a controlled environment using a custom made gas chamber.
Sensor performance was measured in a conductometric mode where the resistance-time
measurements were used to evaluate sensitivity of the material to LP gas. Chronoamperometric
and cyclic voltammetric measurements were used to evaluate the electrochemical performance
for the non-enzymatic glucose sensing.
Firstly, a surfactant free template assisted electrodeposition method was used to fabricate thick
;7-type C112O films having cubic nanostructures and were used for the detection of liquefied
petroleum (LP) gas at low concentrations. Templates were fabricated by initially
electrodepositing a /7-type C112O thin film on a Ti substrate followed by annealing that changed
conductivity of the film to 77-type, as confirmed by Mott-Schottky and spectral response
measurements. SEM measurements of resulting films showed nano-cubic crystals having sizes
of 150-300 nm. When exposed to a mixture of LP gas and dry air, the resistance of these films
increased and the maximum response was recorded when films were maintained at 180°C for
all concentrations and it was independent of the surface morphology. At 180°C, at the lowest
tested LP gas concentration of 2 vol%, a twofold increase in response was observed in the nanocubic
films compared to the micro-crystalline 77-type C112O films. This improvement in gas
response was attributed to the increased effective surface area of the nanostructured films.
Compared to other LP gas sensing materials, these films showed improved response and
recovery times of-120 s and ~90 s, respectively.
Secondly, CU2O and ZnO based nanomaterials having different morphological structures were
developed and used in non-enzymatic glucose sensing. Amperometric sensing measurements
of glucose were performed using 77-C112O nano-cubic films fabricated on Ti using a surfactant
VI
free template aided electrodeposition method. Amperometric measurements for these films
yielded a sensitivity of 28.4 pA mM'1 cm'2 with a lower detection limit (LOD) of 15.6 pM and
a linear range of detection from 17 to 11,650 pM which were significantly better than the
microcrystalline n-C\\iO films. Further, by optimizing the electrodeposition parameters,/7-type
nanocubic CU2O nanostructures were electrodeposited on Cu substrates. These CU2O thin films
were later modified to form copper nanoclusters, with their shapes determined by the
electrodeposition time and the applied potential. Better glucose sensor performance was yielded
by dendrite-like Cu nanoclusters deposited on p-CuiO NCs/Cu electrode with a sensitivity of
45.32 pA mM'1 cm'2, wide linear detection range of 92 to 24,420 pM and a LOD of 31.38 pM
and with a fast response time of less than 3 s. Moreover, to further enhance performance of nonenzymatic
glucose sensing, 3D Cu foam (CF) and 2D Cu plates were used to form binder free
ID Cu(OH)2 nanostructures. Thereafter, following an annealing process Cu(OH)2 structures
were converted to C112O nanostructures with diameter of ~ 200 nm and length exceeding 1 pm.
The CF based nanostructures showed a heterogeneous distribution of nanowires, nanotubes or
nanorods while, Cu plate based nanostructures consisted of ripple-like structures on the outer
surface of the CU2O nanowires. CU2O/CF electrodes yielded a significant improvement in the
sensor performance with a sensitivity of 5,792.69 pA mM'1 cm'2, an ultralow detection limit of
15 nM and a much faster response time of less than 1 s. This outstanding performance can be
attributed to the rough surface of CU2O nanostructures enriched with nano-pores in size of
around 20 nm. At the same time, in the perspective of Langmuir isothermal, ultra-wide linear
detection range of up to 60 mM with a high sensitivity of 1565.19 pA mM'1 cm'2 was measured
for the same electrode. These electrodes provide a better platform for non-enzymatic glucose
detection with high specificity and reproducibility having relative standard deviation (RSD) of
2.8%.
The study was further extended to ZnO nanorods modified with Cu nanoparticles for nonenzymatic
glucose detection. Following co-electrodeposition, fabricated wurtzite structures of
ZnO NRs/ITO electrode with hexagonal facets were modified with Cu NPs in size of less than
100 nm. A sensitivity of 142.41 pA mM'1 cm'2, linear detection range of up to 5,968.1 pM and
a very low LOD of 130 nM was measured for these electrodes. This LOD is one of the best
ever reported for ZnO nanomaterials based on non-enzymatic amperometric glucose sensing